Clearblend® 165
| Category: | MMBS , Methyl Methacrylate Butadiene Styrene |
| Manufacturer: | Styrolution |
| Trademark: | Clearblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ac0i0A_Clearblend-165.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CLEARBLEND 165 is an impact modified styrene acrylic copolymer blend with excellent clarity and outstanding toughness. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 5.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (200°C/5.0 kg) | 5.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.20 to 0.60 | % | ASTM D955 |
| -- | 0.20 to 0.60 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.10 | % | ASTM D570, ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 70 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1520 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 20.7 | MPa | ASTM D638 |
| Yield, 23°C | 21.0 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 50 | % | ASTM D638 |
| Flexural Modulus | |||
| -- | 1550 | MPa | ASTM D790 |
| -- | 1650 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 37.2 | MPa | ASTM D790 |
| -- | 37.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 270 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 93.9 | °C | ASTM D1525 1 |
| Maximum Service Temperature | 250 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index 2 | 1.570 | ASTM D542, ISO 489 | |
| Transmittance (550 nm) | 90.0 | % | ASTM D1003 |
| Haze | 2.2 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 179 to 213 | °C | |
| Middle Temperature | 185 to 218 | °C | |
| Front Temperature | 191 to 224 | °C | |
| Processing (Melt) Temp | 204 to 238 | °C | |
| Mold Temperature | 27.0 to 54.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 1 (10 N) |
| 2 . | Sodium D line |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HF550K | PolyMirae | PP Homopolymer | Moplen |
| Zhongfa PA66 ST-24 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | Nylon 66 | Zhongfa |
| Colorite 12 Series 6512 | Colorite Polymers | PVC, Unspecified | Colorite 12 Series |
| ECP 21150 | TBA Electro Conductive Products Ltd. | TPU-Polyether | ECP |
| EPLAMID 66 MOS2 %2 GFR 30 NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 66 | EPLAMID 66 |