ISPLEN® PC 172 AV
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | REPSOL |
| Trademark: | ISPLEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Abdg1O_ISPLEN-PC-172-AV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene copolymer compound, with 15% calcium carbonate and high melt flow rate. ISPLEN® PC172 AV shows good impact strength an a medium rigidity. It gives high stiffness, and a low warpage and shrinkage behaviour. This product is UV stabilised an antistatic formulated. APPLICATIONS Aesthetic applications which require good gloss surface.
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 14 | g/10 min | ISO 1133 |
| Molding Shrinkage 1 | 1.1 to 1.3 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 66 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 23.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.0 | % | ISO 527-2 |
| Flexural Modulus | 1500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40°C | 1.3 | kJ/m² | |
| -20°C | 1.5 | kJ/m² | |
| 0°C | 2.0 | kJ/m² | |
| 23°C | 3.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -40°C | 36 | kJ/m² | |
| -20°C | 40 | kJ/m² | |
| 0°C | 54 | kJ/m² | |
| 23°C | 110 | kJ/m² | |
| Notched Izod Impact Strength (23°C) | 4.0 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength (23°C) | 90 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 81.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 55.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 146 | °C | ISO 306/A120 |
| -- | 90.0 | °C | ISO 306/B120 |
| Note Message | |
|---|---|
| 1 . | 150x100x3mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVALEN® PH 99 GB 30 LS | Plastcom | PP, Unspecified | SLOVALEN® |
| Fiberfil® PP-60/TC/40/OP WT2595 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Hyosung Polyketone M330A | Hyosung Corporation | PK-Aliphatic | Hyosung Polyketone |
| Iupital® F30-03 | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |
| Hostacom TRC 787N E1 G71535 | LyondellBasell Industries | PP Copolymer | Hostacom |