EL-Lene™ M735RW
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | SCG Chemicals Co., Ltd. |
| Trademark: | EL-Lene™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AbaQXR_EL-Lene-M735RW.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| M735RW and Marvel M70 are linear-low density polyethylene (LLDPE) for rotational molding applications. M735RW is a natural color available in powder and pellet form. With a balance of impact properties, stiffness, and processability. It's suitable for rotational molding of container and general applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.935 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 55 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 19.0 | MPa | ASTM D638 |
| Fracture | 20.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 800 | % | ASTM D638 |
| Bending modulus- Transverse flow 3 | 650 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| ARM Impact 4(-40°C) | 99.0 | J | ARM |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Crystallization Point | 110 | °C | ASTM D2117 |
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 70.0 | °C | ASTM D648 |
| Brittleness Temperature | < -60.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 115 | °C | ASTM D1525 |
| Melting Temperature | 124 | °C | ASTM D2117 |
| Additional Information |
|---|
| UV Resistance Level, ASTM D2565: 8Oven Temperature: 250 to 300°C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 5 mm rotomolded sample |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROMID A 280 MB3 | Taro Plast S.p.A. | Nylon 66 | TAROMID A |
| ADEKA EPR-1415-1 | Adeka Corporation | Epoxy | ADEKA |
| Geon™ Vinyl Flexible F77E | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| EPO-TEK® T905BN-3 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Karina CLEAR PVC COMPOUND -E 75/241-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |