Menzolit® BMC 1000
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Menzolit Ltd (UK) |
| Trademark: | Menzolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AbDSzB_Menzolit-BMC-1000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Menzolit® BMC 1000 is a bulk moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is injection moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens. Menzolit® BMC 1000 is a special BMC for hydrolysis resistant applications. The glass content is set to a level that provides sufficient mouldability with high strength and stiffness properties. Typical applications are components which are exposed to a humid environment. Housings, covers and functional components which are exposed to water or wet atmosphere, like in tropic countries or plant equipment, are typical examples for the use of this material. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.80 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| -- | 0.15 | % | ISO 2577 |
| -- 1 | 0.0 | % | DIN 53464 |
| Water Absorption (Saturation, 23°C) | < 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Compression Molded) | 13000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 36.0 | MPa | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 10000 | MPa | ISO 178 |
| Flexural Stress (Compression Molded) | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Compression Molded) | 30 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 150 | °C | ISO 75-2/A |
| Continuous Use Temperature | 150 | °C | Internal Method |
| Glass Transition Temperature | 125 | °C | DSC |
| CLTE - Flow | 1.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature | 750 | °C | IEC 60695-2-13 |
| Oxygen Index | 22 | % | ISO 4589-2 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Glow Bar | Level BH 2 <= 95 | IEC 60707-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 135 to 150 | °C | |
| Injection Pressure | 2.00 to 8.00 | MPa |
| Note Message | |
|---|---|
| 1 . | Post Molding Shrinkage |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Monprene® OM-12248 | Teknor Apex Company | TPE | Monprene® |
| Toughblend® PP-1400 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PP, Unspecified | Toughblend® |
| Nypol® PA A3 G25 NTLA010 NR342 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| CYCOM® 977-6 | Cytec Industries Inc. | Epoxy | CYCOM® |
| Diakon® TD510 | Lucite International Inc. | Acrylic (PMMA) | Diakon® |