WPP PP PPH5TF2-Natural
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Washington Penn Plastic Co. Inc. |
| Trademark: | WPP PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AavNPY_WPP-PP-PPH5TF2-Natural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| WPP PP PPH5TF2-Natural is a polypropylene homopolymer (PP Homopoly) product, which contains 20% talc filler. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: automotive industry. The main characteristics are: heat stabilizer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 34.0 | MPa | ASTM D638 |
| Yield | 32.0 | MPa | ISO 527-2/5 |
| Yield | 35.0 | MPa | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 2300 | MPa | ASTM D790 |
| -- 3 | 2500 | MPa | ISO 178 |
| Flexural Stress 4 | 50.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 24 | J/m | ASTM D256 |
| -40°C | 1.7 | kJ/m² | ISO 180 |
| 23°C | 2.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 129 | °C | ISO 75-2/B |
| 0.45 MPa, annealed | 130 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 75.0 | °C | ASTM D648, ISO 75-2/Af |
| 1.8 MPa, not annealed | 82.0 | °C | ISO 75-2/A |
| Additional Information |
|---|
| Tested at 23 ± 2°C (73.4 ± 3.6°F) and 50 ± 5% relative humidity unless otherwise noted. |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYMAN® (ABS) HH | A. Schulman Europe | ABS | POLYMAN® |
| TITANZEX® HI2200 | Lotte Chemical Titan (M) Sdn. Bhd. | HDPE | TITANZEX® |
| KumhoSunny PC/PET KCA9360 | Shanghai KumhoSunny Plastics Co., Ltd. | PC+PET | KumhoSunny PC/PET |
| Packalloy LTO™ LTO | Spartech Plastics | Polyolefin, Unspecified | Packalloy |
| Hifax TRC 298P C11301 | LyondellBasell Industries | PP Copolymer | Hifax |