ALCUDIA® LDPE PE-033
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | REPSOL |
| Trademark: | ALCUDIA® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AZtlgH_ALCUDIA-LDPE-PE-033.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCUDIA® PE033 is a low density polyethylene grade, produced by high pressure autoclave technology, suitable for blown or cast film applications. This material offers easy processability and good balance of mechanical and optical properties. It contains antioxidant additive. TYPICAL APPLICATIONS
Recommended melt temperature range from 190-220°C. Processing conditions should be optimised for each production line. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.921 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.30 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | > 0.40 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 200 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 200 µm, blown film | 10.0 | MPa | ISO 527-3 |
| TD : Yield, 200 µm, blown film | 10.0 | MPa | ISO 527-3 |
| MD : Fracture, 200 µm, blown film | 20.0 | MPa | ISO 527-3 |
| TD : Fracture, 200 µm, blown film | 19.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Fracture, 200 µm, blown film | 450 | % | ISO 527-3 |
| TD : Fracture, 200 µm, blown film | 530 | % | ISO 527-3 |
| Dart Drop Impact (200 µm, blown film) | 750 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 200 µm, blown film | 6.0 | N | ISO 6383-2 |
| TD : 200 µm, blown film | 9.0 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 93.0 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45 °, 200 µm, blown film) | 50 | ASTM D2457 | |
| Haze (200 µm, blown film) | 17 | % | ASTM D1003 |
| Additional Information |
|---|
| Data taken from 200 µm thickness film, blow up ratio 2.25:1, frost line height 60 cm. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premier PR350M | Premier Polymers, LLC. | PP Random Copolymer | Premier |
| Sarlink® TPV 6145N | Teknor Apex Company | TPV | Sarlink® TPV |
| Hostacom EKC 133N | LyondellBasell Industries | PP, Unspecified | Hostacom |
| Petrotene® PP B3 TZ PRTA011 PH347 MSP | Petropol Industry and Trade of Polymers LTDA | PP Copolymer | Petrotene® PP |
| Plaslube® PA6 GF30 TL15 | Techmer Engineered Solutions | Nylon 6 | Plaslube® |