Order Products : sales@su-jiao.com
DINAPLEN® PPH1S05 M203
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Grupo Repol |
| Trademark: | DINAPLEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AY9Hsc_DINAPLEN-PPH1S05-M203.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DINAPLEN® PPH1S05 M203 is a Polypropylene Homopolymer (PP Homopolymer) product filled with 20% mineral. It is available in Europe. Primary characteristic: homopolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2600 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 35.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 5.0 | % | |
| Break | 8.5 | % | |
| Flexural Modulus | 1800 | MPa | ISO 178 |
| Flexural Stress | 45.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 50 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 70.0 | °C | ISO 75-2/A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SOLPLAST TC 4000C | UTEKSOL d.o.o. | SBS | SOLPLAST TC |
| Moplen HP553R | LyondellBasell Industries | PP Homopolymer | Moplen |
| Elastron® V V101.A90.B | Elastron USA, Inc. | TPV | Elastron® V |
| Karina BLACK PVC COMPOUND 809D48/1-C-AC-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Polifor® 5020/V2-EP NATURALE | SO.F.TER. SPA | PP Copolymer | Polifor® |