OpteSTAT™ PBT DP492x1

Category: PBT , Polybutylene Terephthalate
Manufacturer: Ovation Polymers Inc.
Trademark: OpteSTAT™
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: AY55CN_OpteSTAT-PBT-DP492x1.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
Electrically conductive Polybutadiene Terephthalate injection molding grade.
General Information
Features
  • Electrically Conductive
Processing Method
  • Injection Molding
PhysicalNominal ValueUnitTest Method
Specific Gravity 1.29g/cm³ASTM D792
MechanicalNominal ValueUnitTest Method
Tensile Modulus 1(23°C)2690MPaASTM D638
Tensile Strength 2(Break, 23°C)47.0MPaASTM D638
Tensile Elongation 3(Break, 23°C)8.8%ASTM D638
Flexural Modulus 4(23°C, 50.0 mm Span)3000MPaASTM D790
Flexural Strength 5(Break, 23°C, 50.0 mm Span)52.0MPaASTM D790
ImpactNominal ValueUnitTest Method
Notched Izod Impact (23°C)91J/mASTM D256
ThermalNominal ValueUnitTest Method
Deflection Temperature Under Load ASTM D648
    0.45 MPa, Unannealed 150°C
    1.8 MPa, Unannealed 56.0°C
ElectricalNominal ValueUnitTest Method
Surface Resistivity 2.6E+5ohmsASTM D257
Volume Resistivity 2.8E+5ohms·cmASTM D257
InjectionNominal ValueUnit
Drying Temperature 80.0 to 90.0°C
Drying Time 2.0hr
Suggested Max Moisture 0.10%
Rear Temperature 190 to 210°C
Middle Temperature 210 to 230°C
Front Temperature 220 to 240°C
Nozzle Temperature 230 to 250°C
Processing (Melt) Temp 240 to 250°C
Mold Temperature 50.0 to 60.0°C
Back Pressure 20.0 to 40.0MPa
Screw Speed 60 to 80rpm
Note Message
1 .50 mm/min
2 .50 mm/min
3 .50 mm/min
4 .1.3 mm/min
5 .1.3 mm/min
Resin Grade Manufacturer Category Trademark
POLYLAN AG1000 POLYMA Kunststoff GmbH & Co. KG ABS POLYLAN
XYFLUOR® 860 Greene, Tweed & Co. Fluorelastomer XYFLUOR®
Hanwha Total PP NH54G HANWHA TOTAL PETROCHEMICALS Co., Ltd. PP, High Crystal Hanwha Total PP
Paracril® BJLT HX INSA NBR Paracril®
Sylvin 8200-85 Brown 7440 Sylvin Technologies Incorporated PVC, Unspecified Sylvin