Viton® B-651C
| Category: | Fluorelastomer , Fluoroelastomer |
| Manufacturer: | DuPont Performance Elastomers |
| Trademark: | Viton® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AY3Csx_Viton-B-651C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Viton®B- 651C is a fluororubber (Fluorelastomer) product,. It can be processed by compression molding and is available in North America or Europe. Viton®The application areas of B- 651C include engineering/industrial accessories, glue/gummed paper, sealing applications and coating applications. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.85 | g/cm³ | ASTM D792 |
| Apparent Density | 1.84 | g/cm³ | ASTM D1895 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 77 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 4.34 | MPa | ASTM D412 |
| Tensile Strength (Yield) | 13.9 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 270 | % | ASTM D412 |
| Compression Set (200°C, 70 hr) | 30 | % | ASTM D395 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Demold Time | |||
| 177°C | 10 | min | |
| 230°C | 1400 | min |
| Additional Information |
|---|
| Nominal Viscosity, ML 1 + 10, 121°C: 60Polymer Fluorine Content: 68.5% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 283 TFE 18 SI 2 | RTP Company | Nylon 66 | RTP |
| Propilven F-409 | Propilven, S.A. | PP Homopolymer | Propilven |
| NEXT SIGNATURE CAP MG-100 | NEXT Specialty Resins, Inc. | CAP | NEXT SIGNATURE |
| P84® NT1 15G | Evonik Industries AG | PI, TP | P84® |
| LEXAN™ LUX7430C resin | SABIC Innovative Plastics | PC | LEXAN™ |