NYCOA Polyamide 589
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AXtR8D_NYCOA-Polyamide-589.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 589 is an ultra-high viscosity Nylon 6 resin for extrusion processing. It retains good melt strength even at high processing temperatures. This trait makes it suitable for blow molding and blown film processing. Typical applications include profile NYCOA 589 also features very good toughness and resistance to chemical attack. NYCOA 589 complies with all the requirements of the FDA regulations 21 CFR 177.1500. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 1.7 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 89.6 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 150 | % | ASTM D638 |
| Flexural Modulus 3 | 2700 | MPa | ASTM D790 |
| Flexural Strength 4 | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 191 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 68.3 | °C | ASTM D648 |
| Melting Temperature | 221 | °C | DSC |
| Additional Information |
|---|
| Relative Viscosity, NYCOA Method: 5 to 5.5 SAVWater Extractable, NYCOA Method: 0.8 %The value listed as Melting Point DSC, was tested in accordance with ASTM D789. |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® B 218L V30 BLACK 44 N | Solvay Engineering Plastics | Nylon 66/6 | TECHNYL® B |
| Taitacell EPS 321LS | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| Geon™ Vinyl Fittings M1015 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Fittings |
| ENFLEX VL-120-85A | Ravago Group | PP+EPDM | ENFLEX |
| HIPTEN® 22003 | HIP-PetroHemija | LDPE | HIPTEN® |