Smooth-Cast® ColorMatch® 325
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Smooth-On, Inc |
| Trademark: | Smooth-Cast® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AXrcg5_Smooth-Cast-ColorMatch-325.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The Smooth-Cast® 325, 326 & 327 ColorMatch® Series plastics are fast-cast resins that were developed specifically for adding color pigments and fillers to achieve true color representation or filler effect. The ColorMatch® Series is formulated "color neutral". Small amounts of pigment will yield accurate, vivid colors from cured castings using So-Strong® tints or Ignite® color pigments. The ColorMatch® Series offers the convenience of a 1A: 1B mix ratio by volume and has a very low viscosity. Demold times range from about 10 minutes to 2-4 hours (depending on product, mass and mold configuration). Note: Large mass castings will get very hot and shrink more, depending on mold configuration. The ColorMatch® Series also readily accept fillers (such as URE-FIL® 3 from Smooth-On). Because of its neutral color, Smooth-Cast® 325 is ideal for creating marble and wood grain casting effects, or duplicating the look of real metal by adding bronze, brass or other metal powder (see Smooth-On technical bulletin for metal cold casting). Applications for the ColorMatch® Series plastics include making pigmented prototype models or figures, special effect props, reproducing small to medium size sculptures, decorative jewelry, etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D1475 |
| Specific Volume | 0.936 | cm³/g | ASTM D1475 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mixing Ratio | 115A:100B by weight 1A:1B Volume |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 1.0 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 72 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 965 | MPa | ASTM D638 |
| Tensile Strength | 21.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 | % | ASTM D638 |
| Flexural Modulus | 69.6 | MPa | ASTM D790 |
| Flexural Strength | 25.4 | MPa | ASTM D790 |
| Compressive Modulus | 252 | MPa | ASTM D695 |
| Compressive Strength | 24.1 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 48.9 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pot Life | 2.5 | min | |
| Thermoset Mix Viscosity | 100 | cP | ASTM D2393 |
| Demold Time 1(23°C) | 10 | min |
| Note Message | |
|---|---|
| 1 . | Cure Time |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ FR PP301 SHI BK268 | PolyOne Corporation | PP, Unspecified | Maxxam™ FR |
| POLYLAN AG10NP | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| Flontech® FT-GL15-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| LNP™ LUBRICOMP™ RFP48SXS compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |
| Moplen EP300H | LyondellBasell Industries | PP Impact Copolymer | Moplen |