Pearlbond™ D1160
| Category: | TPU, Unspecified , Thermoplastic Polyurethane Elastomer |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Pearlbond™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AXkZ94_PearlbondD1160.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Pearlbond™ D1160 is a linear, aromatic polyurethane, supplied in form of small white granules, which combines a high crystallization rate and high thermoplasticity level. APPLICATIONS Pearlbond™ D1160 is used for obtaining PU films by extrusion (blow and cast) for solvent-free adhesion, by heat-seal process. Once activated, the films provide bonds with high initial values, and which have good heat resistance. The adhesion to PVC, rubber and polyurethane materials, as well as to a variety of fabrics, is excellent. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.18 | g/cm³ | ASTM D792 |
| 20°C | 1.18 | g/cm³ | ISO 2781 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 10 - 20 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 90 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| -- | 30.0 | MPa | ISO 527-2 |
| 100% strain | 5.00 | MPa | ISO 527-2 |
| 300% strain | 6.00 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 720 | % | ISO 527-2 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 5.00 | MPa | ASTM D412 |
| 300% strain | 6.00 | MPa | ASTM D412 |
| Tensile Strength | 30.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 720 | % | ASTM D412 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 90.0 - 95.0 | °C | Internal method |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bruck field viscosity- 15% MEK (20°C) | 0.550 - 1.50 | Pa·s | Internal method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Crystallization Rate | High | Internal method | |
| Softening Range | 80 - 85 | °C | Internal method |
| Thermoplasticity | High | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Extruder Screw L/D Ratio | 25.0:1.0 | ||
| Extruder Screw Compression Ratio | 3.0:1.0 | ||
| Drying Temperature | 40 - 50 | °C | |
| Drying Time | 3.0 - 6.0 | hr | |
| Cylinder Zone 1 Temp. | 115 - 125 | °C | |
| Cylinder Zone 2 Temp. | 200 - 210 | °C | |
| Cylinder Zone 3 Temp. | 200 - 210 | °C | |
| Cylinder Zone 4 Temp. | 170 - 180 | °C | |
| Die Temperature | 170 - 180 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravamid® AGF30 BK45 | Ravago Group | Nylon 66 | Ravamid® |
| Quadrant EPP Delrin® AF Blend | Quadrant Engineering Plastic Products | Acetal (POM) Homopolymer | Quadrant EPP |
| Scolefin 73 C 20-8 | Ravago Group | PP Copolymer | Scolefin |
| Moplen EPQ30M | Shazand (Arak) Petrochemical Corporation | PP Copolymer | Moplen |
| ACCUTECH™ HP0339G20M10CL | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |