InnoPlus LL7410D
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | PTT Global Chemical Public Company Limited |
| Trademark: | InnoPlus |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AXA8mG_InnoPlus-LL7410D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
InnoPlus LL7410D resin is a linear low density polyethylene with butene comonomers, with high content of slip and antiblock. This grade offers the excellent machinability on conversion lines. Films extruded from InnoPlus LL7410D have high tensile strength, elongation, good toughness and outstanding puncture strength. It is available for tubular blown film processing. InnoPlus LL7410D is recommended for producing general purpose films, liners, food packaging, heavy duty and agricultural films. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.921 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 52 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, Compression Molded | 11.0 | MPa | |
| Break, Compression Molded | 28.0 | MPa | |
| Tensile Elongation (Break, Compression Molded) | 790 | % | ASTM D638 |
| Flexural Modulus (Compression Molded) | 310 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 25 µm, Blown Film | 190 | MPa | |
| 1% Secant, TD : 25 µm, Blown Film | 220 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 25 µm, Blown Film | 34.0 | MPa | |
| TD : Break, 25 µm, Blown Film | 26.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm, Blown Film | 700 | % | |
| TD : Break, 25 µm, Blown Film | 900 | % | |
| Dart Drop Impact (25 µm, Blown Film) | 90 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, Blown Film | 100 | g | |
| TD : 25 µm, Blown Film | 350 | g |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 440 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 97.0 | °C | ASTM D1525 |
| Peak Melting Temperature | 121 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 50 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 17 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 to 180 | °C | |
| Die Temperature | 170 to 190 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9056-80 BLACK | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Titalon® 4182TFS | Titan Plastics Compounds Co., Ltd. | Nylon 46 | Titalon® |
| Evoprene™ GC 5619 | AlphaGary | SEBS | Evoprene™ GC |
| PERCOM® XG1248 | A. Schulman Europe | PP, Unspecified | PERCOM® |
| PermaStat® 1200 T-70A | RTP Company | TPU-Polyether | PermaStat® |