EMERGE™ PC 8130-10
| Category: | PC , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AWikqH_EMERGEPC813010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EMERGE™ PC 8130 Advanced Resin is an ignition-resistant polycarbonate resin with improved UV stability. It is designed for thin-wall applications and has a UL94 V-0 rating at 1.0 mm. EMERGE PC 8130 is also f1 rated according to UL 746C. This resin does not contain chlorine or bromine additives. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 - 0.70 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.15 | % | ASTM D570 |
| Outdoor Suitability | f1 | UL 746C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2380 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield | 61.4 | MPa | ASTM D638 |
| Yield | 61.0 | MPa | ISO 527-2/50 |
| Fracture | 58.6 | MPa | ASTM D638 |
| Fracture | 59.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 6.0 | % | ASTM D638 |
| Fracture | 120 | % | ASTM D638 |
| Flexural Modulus | 2330 | MPa | ASTM D790 |
| Flexural Strength | 97.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 690 | J/m | ASTM D256 |
| Instrumented Dart Impact | 62.1 | J | ASTM D3763 |
| Tensile Impact Strength | 630 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 137 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 127 | °C | ASTM D648 |
| Vicat Softening Temperature | 151 | °C | ASTM D1525 |
| CLTE - Flow | 6.5E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 115 | °C | UL 746 |
| RTI | 130 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Arc Resistance | PLC 7 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 0.9 mm | PLC 2 | UL 746 | |
| 1.0 to 3.0mm | PLC 1 | UL 746 | |
| High Voltage Arc Resistance to Ignition (HVAR) | PLC 1 | UL 746 | |
| Hot-wire Ignition (HWI) (0.9 to 3.0mm) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | Internal method | ||
| 0.9 mm, all 1 | V-1 | Internal method | |
| 0.9 mm, wt, black 2 | V-0 | Internal method | |
| 1.0 mm, all 3 | V-0 | Internal method | |
| 2.0 mm, all 4 | 5VB | Internal method | |
| 3.0 mm, all 5 | 5VA | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Processing (Melt) Temp | 288 - 302 | °C |
| Note Message | |
|---|---|
| 1 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 2 . | This rating is not intended to reflect the danger caused by this or any other material under actual fire conditions. |
| 3 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 4 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 5 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pyramid™ PEEK KD2000 Injection Molded Shape | Polymics, Ltd. | PEEK | Pyramid™ PEEK |
| TECHNO MUH E1300 | Techno Polymer Co, Ltd. | ABS | TECHNO MUH |
| Sumiflex® QE QE131ATH | Mitsubishi Chemical Corporation | TES | Sumiflex® QE |
| ULTEM™ 2300R resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| Akulon® S223-E | DSM Engineering Plastics | Nylon 66 | Akulon® |