RELENE® E24065
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Reliance Industries Limited |
| Trademark: | RELENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AWY5hH_RELENE-E24065.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| E24065, is a butene comonomer based Linear Low Density Polyethylene. This grade is designed for extrusion coating applications. It offers excellent sealing properties, ESCR, tear strength and abrasion resistance in thin extrusion coatings. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.5 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic, Blown Film | 0.69 | ||
| vs. Itself - Static, Blown Film | 0.79 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 40 µm, Blown Film | 12.0 | MPa | |
| TD : Yield, 40 µm, Blown Film | 11.5 | MPa | |
| MD : Break, 40 µm, Blown Film | 25.0 | MPa | |
| TD : Break, 40 µm, Blown Film | 20.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 40 µm, Blown Film | 620 | % | |
| TD : Break, 40 µm, Blown Film | 750 | % |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer SV-56000U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| ALCOM® PC 740/4 UV WT1102-04LD | ALBIS PLASTIC GmbH | PC | ALCOM® PC |
| NHU-PPS 21605C/F | Zhejiang NHU Comp. Ltd. | PPS | NHU-PPS |
| Sylvin 9219-75 White 1485 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| XENOY™ 5720U resin | SABIC Innovative Plastics | PC+PBT | XENOY™ |