Order Products : sales@su-jiao.com
Laramid G/45
| Category: | PPA , Polyphthalamide |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Laramid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AW5gIA_Laramid-G-45.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Semi-aromatic polyammide. Glass fibres. Very good thermal properties. Good chemical resistance. Low moisture absorption. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.55 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.70 to 1.0 | % | |
| Flow : 2.00 mm | 0.25 to 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 16000 | MPa | |
| 60°C | 11200 | MPa | |
| 90°C | 8500 | MPa | |
| 120°C | 6700 | MPa | |
| 150°C | 5800 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 245 | MPa | |
| Break, 60°C | 195 | MPa | |
| Break, 90°C | 170 | MPa | |
| Break, 120°C | 150 | MPa | |
| Break, 150°C | 95.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 2.5 | % | |
| Break, 60°C | 3.0 | % | |
| Break, 90°C | 3.8 | % | |
| Break, 120°C | 6.0 | % | |
| Break, 150°C | 7.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 85 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 100 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 290 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 280 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 140 | °C | |
| Vicat Softening Temperature | 275 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 5.0E-6 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 310 to 340 | °C | |
| Mold Temperature | 150 to 170 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Geon™ HTX Ultra LA425 | PolyOne Corporation | PVC Alloy | Geon™ HTX Ultra |
| Elastron® G G500.A40.B.ABS | Elastron USA, Inc. | SEBS | Elastron® G |
| Eleme NGL070LG | Eleme Petrochemical Company Ltd | LLDPE | Eleme |
| CYCOLOY™ MC8800 resin | SABIC Innovative Plastics | PC+ABS | CYCOLOY™ |
| Sylvin 8785-80 Brown 7357 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |