ACCUCOMP™ HD0202L
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AVvFg8_ACCUCOMP-HD0202L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUCOMP™ HD0202L is a High Density Polyethylene product. It is available in North America. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.950 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.8 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 50 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1000 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 25.0 | MPa | |
| Break | 16.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 10 | % | |
| Break | 550 | % | |
| Flexural Modulus | 800 | MPa | ASTM D790 |
| Flexural Strength | 21.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 140 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 78.0 | °C | |
| 1.8 MPa, Unannealed | 44.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ADDILENE H 526 N30 | ADDIPLAST | PP Homopolymer | ADDILENE |
| BP RRP 3009 GK BLK | Buckeye Polymers, Inc. | PP, Unspecified | BP |
| HiFill® PA6 GF33 IM L | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Jam HDPE HM5010T3N NATURAL | Jam Petrochemical Company | HDPE | Jam HDPE |
| SIBUR Synthetic Rubber SBR-1706 Grade D | SIBUR | SBR, Emulsion | SIBUR Synthetic Rubber |