RTP 200 F
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AVD60V_RTP-200-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unfilled |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.02 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.6 - 2.0 | % | ASTM D955 |
| Moisture Content | 0.10 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1380 | MPa | ASTM D638 |
| Tensile Strength | 41.4 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 10 | % | ASTM D638 |
| Flexural Modulus | 1310 | MPa | ASTM D790 |
| Flexural Strength | 48.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 1400 | J/m | ASTM D4812 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 4.0 | hr | |
| Dew Point | -40.0 | °C | |
| Processing (Melt) Temp | 221 - 274 | °C | |
| Mold Temperature | 65.6 - 104 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SureSpec LD20-250 | Genesis Polymers | LDPE | SureSpec |
| APEX® 3701-70NT1 | Teknor Apex Company | PVC, Flexible | APEX® |
| Fainplast PVC MGS 80/T | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| LUVOCOM® 16-8699 | Lehmann & Voss & Co. | PARA | LUVOCOM® |
| OPTODYNE™ UV-3200 | DAIKIN AMERICA, INC. | Epoxy | OPTODYNE™ |