SCHULABLEND® SCHULABLEND® (ABS/PA) M/MK 7102 GF20
| Category: | ABS+Nylon , Acrylonitrile Butadiene Styrene + PA |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULABLEND® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AV3rCP_SCHULABLENDSCHULABLENDABSPAMMK7102GF20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% glass fibre reinforced ABS/PA blend |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) | 3.00 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 77.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/1A/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 34 | kJ/m² | ISO 179/1eU |
| 23°C | 36 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 179 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 130 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 213 | °C | ISO 306/A50 |
| -- | 150 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | ISO 3795 |
| Flammability Classification (1.5 mm) | HB | IEC 60695-11-10, -20 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.040 - 0.10 | % | |
| Suggested Max Regrind | 20 | % | |
| Processing (Melt) Temp | 230 - 270 | °C | |
| Mold Temperature | 40 - 80 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reslen PPH 20GF GWT 960 | Polimarky Spolka Jawna | PP Homopolymer | Reslen |
| 3M™ Dyneon™ Fluoroplastic THV 500GZ | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroplastic |
| HiFill® TPU/I GF40 | Techmer Engineered Solutions | TPU-Polyether | HiFill® |
| Iupilon® EGN2020KR | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| TOTAL Polyethylene Bio TPSeal® 0650_03 | TOTAL Refining & Chemicals | mPE | TOTAL Polyethylene |