ESTOPLAST XU 425NGY148
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Ester Industries Ltd. |
| Trademark: | ESTOPLAST XU |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AUupgN_ESTOPLASTXU425NGY148.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyamide 6 - Mineral and Glass Fiber Reinforced, 25% Automotive: Intake manifold, Engine, Powertrain, Exterior trim, Interior trim, Electrical components and connectors Electrical & Electronic: Low voltage switch gear/power distribution, Lighting, Power connectors , MCB, |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 5.0 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.95 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 65.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.3 | % | ASTM D638 |
| Flexural Strength | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 30 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 185 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 180 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (2.00 mm) | 22 | kV/mm | ASTM D149 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.2 mm | 960 | °C | IEC 60695-2-12 |
| 3.0 mm | 960 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85 - 90 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 235 - 245 | °C | |
| Middle Temperature | 235 - 250 | °C | |
| Nozzle Temperature | 235 - 255 | °C | |
| Processing (Melt) Temp | 235 - 260 | °C | |
| Mold Temperature | 55 - 80 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 FR MS HS | RTP Company | Nylon 66 | RTP |
| TECHNO ABS ZF5551 | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| TAIRIPRO T1202 | Formosa Plastics Corporation | PP Homopolymer | TAIRIPRO |
| Hifax TYC007P | LyondellBasell Industries | TPO (POE) | Hifax |
| Karina IVORY PVC COMPOUND 800-35/ 2-BYR-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |