TOTAL Polypropylene PPC 2660
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polypropylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AUisQm_TOTAL-Polypropylene-PPC-2660.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Total Petrochemicals PPC 2660 is a heterophasic copolymer polypropylene with a Melt Flow Index of 0.8 g/min for the manufacturing of films with very good mechanical properties in the blown process. Polypropylene PPC 2660 is characterized by a low fluidity hence good melt strength to provide ease of processing and good manufactured article properties. Polypropylene PPC 2660 is suitable particularly for the extrusion of corrugated cardboard, blown film, sheet and pipes and for blow-moulding applications where a very high impact resistance is required. Polypropylene PPC 2660 is intended for applications requiring high mechanical properties like heavy duty bags, lamination films, retortable food packaging. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Apparent Density | 0.53 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.80 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 74 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1200 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 24.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 13 | % | ISO 527-2 |
| Flexural Modulus | 1100 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Stress - MD | ISO 527-3 | ||
| Yield, 30 µm, Blown Film | 30.0 | MPa | |
| Break, 40 µm, Blown Film | 80.0 | MPa | |
| Tensile Elongation - MD (Break, 40 µm, Blown Film) | 600 | % | ISO 527-3 |
| Dart Drop Impact (40 µm, Blown Film) | 100 | g | ISO 7765-1 |
| Elmendorf Tear Strength 1 | ISO 6383-2 | ||
| MD : 40.0 µm | 5.0 | kN/m | |
| TD : 40.0 µm | 45.0 | kN/m |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 6.0 | kJ/m² | |
| 23°C | > 50 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180 | ||
| -20°C | 6.0 | kJ/m² | |
| 23°C | > 50 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 88.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 50.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 148 | °C | ISO 306/A50 |
| -- | 70.0 | °C | ISO 306/B50 |
| Melting Temperature (DSC) | 165 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (40.0 µm, Blown Film) | 14 | ASTM D2457 | |
| Haze (40.0 µm, Blown Film) | 41 | % | ISO 14782 |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radel® R-5500 | Solvay Specialty Polymers | PPSU | Radel® |
| Niuk 23RN60 | Shanghai Niuk New Plastic Technology Co., Ltd. | PC+ABS | Niuk |
| alphalon™ 27 D | Grupa Azoty ATT Polymers GmbH | Nylon 6 | alphalon™ |
| ANYPOL CL-160LL | SH Energy & Chemical | PS (EPS) | ANYPOL |
| LNP™ LUBRICOMP™ DX09407H compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |