INTREPID™ 2498 BK
| Category: | HDPE , Bimodal Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | INTREPID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AUOlfx_INTREPID-2498-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INTREPID™ 2498 BK Bimodal Polyethylene Resin is produced using UNIPOL™ II process technology. This product is intended for use in industrial piping system where extreme conditions such as high pressures, elevated temperatures and aggressive chemicals or hydrocarbons exist. Suitable uses include oil & gas field pipelines, gas distribution pipelines, and other industrial applications. Industrial Standards Compliance: ASTM D 3350: cell classification
NOTES: (1) The first five numbers of the cell classification are based on natural resin. The last number and letter are based on black resin (natural resin plus 6.5% DFNF-0092 BK). |
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| Natural | 0.949 | g/cm³ | |
| Black 1 | 0.959 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.080 | g/10 min | |
| 190°C/21.6 kg | 7.0 | g/10 min |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | > 24.1 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | > 500 | % | ASTM D638 |
| Flexural Modulus | 1030 | MPa | ASTM D790B |
| Creep Rupture Strength - 1798 psi (12.4 MPa) (20°C) | > 200 | hr | ISO 1167 |
| Hydrostatic Strength 4 | ISO 4427 | ||
| 1798 psi (12.4 MPa) : 20°C | > 200 | hr | |
| 725 psi (5.0 MPa) : 80°C | > 1000 | hr | |
| Resistance to Rapid Crack Propagation, Pc | |||
| Calculated, Full Scale : 0°C 5 | > 46.0 | bar | ISO 13478 |
| S-4 : 0°C 6 | > 12.0 | bar | ISO 13477 |
| Resistance to Rapid Crack Propagation, Tc - S-4 @ 10 bar 7 | < -17 | °C | ISO 13477 |
| Resistance to Short-Time Hydraulic Pressure | > 27.6 | MPa | ASTM D1599 |
| Slow Crack Growth PENT 8 | > 10000 | hr | ASTM F1473 |
| Stress Crack Resistance - Pipe notch (80°C) 9 | > 1000 | hr | ISO 13479 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermal Stability | > 220 | °C | ASTM D3350 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 10(23°C) | 490 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature 11 | < -75.0 | °C | ASTM D746A |
| Note Message | |
|---|---|
| 1 . | Natural resin extruded under proper conditions with carbon black masterbatch DFNF-0092 (6.5%). |
| 2 . | Compression molded parts prepared according to ASTM D 4703 Procedure C unless otherwise noted in the test method. Properties will vary with changes in molding conditions and aging time. |
| 3 . | Compression molded parts prepared according to ASTM D 4703 Procedure C unless otherwise noted in the test method. Properties will vary with changes in molding conditions and aging time. |
| 4 . | Natural resin extruded under proper conditions with carbon black masterbatch DFNF-0092 (6.5%). |
| 5 . | Calculated value, determined by the equation in ISO 4437 based on S-4 test data. Pipe diameter of 10 inch IPS (25.4 cm) and Standard Diameter Ratio (SDR) 11 |
| 6 . | Pipe diameter of 10 inch IPS (25.4 cm) and Standard Diameter Ratio (SDR) 11. |
| 7 . | Pipe diameter of 10 inch IPS (25.4 cm) and Standard Diameter Ratio (SDR) 11. |
| 8 . | Compression molded parts prepared according to ASTM D 4703 Procedure C unless otherwise noted in the test method. Properties will vary with changes in molding conditions and aging time. |
| 9 . | 133 psi (0.92 MPa) |
| 10 . | Compression molded parts prepared according to ASTM D 4703 Procedure C unless otherwise noted in the test method. Properties will vary with changes in molding conditions and aging time. |
| 11 . | Compression molded parts prepared according to ASTM D 4703 Procedure C unless otherwise noted in the test method. Properties will vary with changes in molding conditions and aging time. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE PCG00 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| Spartech Polycom X05030 | Spartech Polycom | PP, Unspecified | Spartech |
| T-Blend® 6594N-G68E-A | TSRC Corporation | SEBS | T-Blend® |
| Elastollan® 1147 D FHF | BASF Polyurethanes GmbH | TPU-Polyether | Elastollan® |
| LNP™ STAT-KON™ DD0009P compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |