CAPXIDAN™ HD
| Category: | Ethylene Copolymer , Ethylene Copolymer |
| Manufacturer: | NWP, Inc. |
| Trademark: | CAPXIDAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AUMgEE_CAPXIDAN-HD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CAPXIDAN™ HD is a Modified Copolymer produced with a proprietary, specialized formulation. It is designed to be coextruded over Wood-Plastic Composite (WPC) deck boards to provide moisture, stain, wear resistance, aesthetics, durability at elevated temperatures, and unprecedented adhesion to the WPC substrate. CAPXIDAN™ HD is a two-component capstock system. The CAPXIDAN™ resin should be extruded together with a specific synergistic additive masterbatch in the recommended proportion of 98:2 by weight. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.950 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2 | ||
| -40°C | 2310 | MPa | |
| 0°C | 1690 | MPa | |
| 23°C | 862 | MPa | |
| Tensile Strength | ASTM D638 | ||
| Yield | 20.0 | MPa | |
| Break | 21.0 | MPa | |
| Tensile Elongation (Break) | 400 | % | ASTM D638 |
| Flexural Modulus | ISO 178 | ||
| -40°C | 517 | MPa | |
| 0°C | 379 | MPa | |
| 23°C | 207 | MPa |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 124 | °C | ASTM D1525 |
| CLTE - Flow (-100 to 85°C) | 1.5E-4 | cm/cm/°C | ASTM D696 |
| Specific Heat (23°C) | 1920 | J/kg/°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sevrene® 4500-70A | Vi-Chem Corporation | TPE | Sevrene® |
| Sinvicomp DFR5806 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| SWANCOR Epoxy 901-2T | SWANCOR IND. CO., LTD. | Epoxy | SWANCOR Epoxy |
| EVALENE® PP PHF0301 | JG Summit Petrochemical Corporation | PP Homopolymer | EVALENE® PP |
| Multilon® R-2020 | TEIJIN LIMITED | PC+ABS | Multilon® |