POCAN® B 1300 000000
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LANXESS Corporation |
| Trademark: | POCAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AU2zvd_POCAN-B-1300-000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT, non-reinforced, injection molding,Extrusion |
| General Information | |
|---|---|
| Agency Ratings |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.30 | g/cm³ | ISO 1183 |
| Apparent Density | 0.80 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 45.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Across Flow : 260°C, 3.00 mm 1 | 1.9 | % | ISO 2577 |
| Across Flow : 150°C, 48 hr, 3.00 mm 2 | 0.50 | % | ISO 294-4 |
| Flow : 260°C, 3.00 mm 3 | 1.9 | % | ISO 2577 |
| Flow : 150°C, 48 hr, 3.00 mm 4 | 0.50 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.50 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % | |
| Viscosity Number (Reduced Viscosity) | 105.0 | ml/g | ISO 1628 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 120 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2700 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 55.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 8.0 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | > 20 | % | ISO 527-2/50 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 2400 | MPa | |
| 1000 hr | 1400 | MPa | |
| Flexural Modulus 5(23°C) | 2700 | MPa | ISO 178/A |
| Flexural Stress 6 | |||
| 3.5% Strain | 75.0 | MPa | ISO 178/A |
| 23°C | 90.0 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 7(23°C) | 6.0 | % |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Electrolytical Corrosion | A 1 | IEC 60426 | |
| ISO Shortname | PBT, GN, 10-030 | ISO 7792 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.0 to 0.020 | % | Karl Fisher |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Puncture Energy | ISO 6603-2 | ||
| -- 8 | 15.0 | J | |
| -- 9 | 40.0 | J | |
| Film Puncture Force 10 | 3860 | N | ISO 6603-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | < 10 | kJ/m² | |
| 23°C | < 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 150 | kJ/m² | |
| 23°C | 220 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | < 10 | kJ/m² | |
| -30°C | < 10 | kJ/m² | |
| 23°C | < 10 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 150 | kJ/m² | |
| 23°C | 150 | kJ/m² | |
| Multi-Axial Instrumented Impact Peak Force (23°C) | 110 | N | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 160 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 60.0 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 45.0 | °C | ISO 75-2/C |
| Vicat Softening Temperature | 180 | °C | ISO 306/B50 |
| Ball Pressure Test (190°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature 11 | 225 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 1.2E-4 | cm/cm/°C | |
| Transverse : 23 to 55°C | 1.3E-4 | cm/cm/°C | |
| Thermal Conductivity (23°C) | 0.25 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electric Strength (23°C, 1.00 mm) | 28 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.40 | ||
| 23°C, 1 MHz | 3.20 | ||
| Comparative Tracking Index | IEC 60112 | ||
| Solution A | 600 | V | |
| Solution B | 300 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.60 mm | HB | ||
| Glow Wire Flammability Index (2.00 mm) | 750 | °C | IEC 60695-2-12 |
| Oxygen Index 12 | 24 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Circulation Dryer | 120 | °C | |
| Drying Time - Circulation Dryer | 4.0 to 8.0 | hr |
| Note Message | |
|---|---|
| 1 . | 150x150x3; MT 80°C; 600 Bar |
| 2 . | 150x105x3 |
| 3 . | 150x150x3; MT 80°C; 600 Bar |
| 4 . | 150x150x3 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Pull Rate: 2 mm/min; 50% RH |
| 8 . | -30°C |
| 9 . | 23°C |
| 10 . | -30°C |
| 11 . | 10°C/min |
| 12 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene MBW0741M | Teknor Apex Asia Pacific PTE. LTD. | LLDPE | Sinpolene |
| Witcom PP C/4G-EC-EM-HS | Witcom Engineering Plastics B.V. | PP Copolymer | Witcom PP |
| XANTAR® G8F 23 UR | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Chemlon® A60XT | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| LNP™ THERMOCOMP™ RF00AS compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |