Purell HM671T
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Purell |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ATmopU_Purell-HM671T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Without exception, all potential activities for applications in the pharmaceutical, medical device, laboratory and diagnostics area have to be discussed with the relevant Technical (P & AD) and Business contacts first. To discuss a medical/pharmaceutical application please contact: your local Distributor or your local Basell contact. Purell HM671T is a high fluidity metallocene-catalysed polypropylene. It is nucleated and has a gamma - ray stabilizing additivation. Purell HM671T is a medical grade designed for injection moulding applications in medical after approval is given by Basell. Purell HM671T exhibits a very high stiffness combined with an excellent transparency and out-standing organoleptic properties. Its very narrow molecular weight distribution makes it particularly suitable for distortion-free mouldings. Purell HM671T is applied in high transparency and rigid pharmaceutical and diagnostic applications such as well and microtitre plates, measuring cups and labware. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 60 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 80.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 73.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1700 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 33.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield, 23°C | 9.0 | % | |
| Break, 23°C | > 50 | % | |
| Flexural Modulus (23°C) | 1550 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180 | ||
| -20°C | 1.0 | kJ/m² | |
| 0°C | 2.0 | kJ/m² | |
| 23°C | 3.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 94.0 | °C | ASTM D648, ISO 75-2/B |
| Vicat Softening Temperature | |||
| -- | 135 | °C | ISO 306/A50 |
| -- | 87.0 | °C | ISO 306/B50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (1000 µm) | 10 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Methylon 75202 | Durez Corporation | Phenolic | Methylon |
| 4DUR® 9K34200 H | 4Plas | PBT | 4DUR® |
| Adell Polyamide BJ-33 Glass Reinforced Mineral Filled | Adell Plastics, Inc. | Nylon 6 | Adell Polyamide |
| INNOMID® CS 6-9830 | Inno-Comp Ltd. | Nylon 6 Alloy | INNOMID® |
| LEXAN™ XHT5141 resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |