ENVIROPLAS® ENV14-NC810
| Category: | PC , Polycarbonate |
| Manufacturer: | ENVIROPLAS®, Inc. |
| Trademark: | ENVIROPLAS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ATe1To_ENVIROPLAS-ENV14-NC810.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Injection Molding Grade, Non-Bromine - Non-Chlorine Flame retardant, Impact Modified, w/Mold Release, UV Stabilized. Ideal for Outdoor Exposure Applications Requiring Ignition, Hydrolytic and UV Resistance along with Thermal Performance. NC810 = To Be Assigned 5 Digit Number Indicating Natural, Black, or Custom Color. Contact Enviroplas regarding UL recognized versions of this product. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 16 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 60.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 120 | % | ASTM D638 |
| Flexural Modulus | 2340 | MPa | ASTM D790 |
| Flexural Strength | 89.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 770 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 121 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | Internal Method | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 254 to 277 | °C | |
| Middle Temperature | 254 to 277 | °C | |
| Front Temperature | 254 to 277 | °C | |
| Nozzle Temperature | 243 to 266 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.00 to 0.345 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Viton® A-361C | DuPont Performance Elastomers | Fluorelastomer | Viton® |
| TROSIFOL® VG FR | Kuraray Co., Ltd. | PVB | TROSIFOL® |
| E-Pos 328 | Epocat Nederland BV | Epoxy | E-Pos |
| INEOS PP 100-HR25 | INEOS Olefins & Polymers Europe | PP Homopolymer | INEOS PP |
| SHINSTRA AG30TKB (PA6) | Shinil Chemical Industry Co., Ltd. | Nylon 6 | SHINSTRA |