DM® BSR-06®
| Category: | Biodeg Polymers , Biodegradable Polymers |
| Manufacturer: | Shanghai Disoxidation Enterprise Development Co., Ltd. |
| Trademark: | DM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ATZPU7_DM-BSR-06-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Having the same technical and mechanical properties as conventional polyethylene, BSR-06® is a bio-based product engineered for blown film applications. BSR-06® has been developed as a hybrid resin with use of raw materials from agricultural resources and polyethylene. With the same elongation and tensile strength of polyethylene, BSR-06® complies with ISO14855 standards which with good biodegradability. BSR-06® will be biodegraded more than 63% with the period of 90~180 days, breaking into non-toxic grains and continue decomposing in the earth. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 to 1.18 | g/cm³ | GB/T 1033 |
| Melt Mass-Flow Rate (MFR) | 0.80 to 1.5 | g/10 min | GB/T 3682 |
| Moisture Content | < 1.0 | % | Internal Method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Biobased Content | > 62 | % | Internal Method |
| Biodegradability - 122 days | > 62 | % | ISO 14855 |
| Hexane Extraction | < 4.00 | GB/T 5009 | |
| Starch Content | > 35 | % | Internal Method |
| Tear Strength - Right Angle | > 40.0 | MPa | GB/T 1040 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | GB/T 1040 | ||
| Across Flow | 25.6 | MPa | |
| Flow | 33.0 | MPa | |
| Tensile Elongation | GB/T 1040 | ||
| Across Flow : Break | 560 | % | |
| Flow : Break | 380 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | > 65.0 | °C | GB/T 1633 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRE-ELEC® TPU 1510 | Premix Oy | TPU, Unspecified | PRE-ELEC® |
| TEKAFIN™ PB75 | Mando Advanced Materials Co., Ltd. | PP, Unspecified | TEKAFIN™ |
| Electrafil® TPX-PPO/HIPS-03015 | Techmer Engineered Solutions | PPE+PS | Electrafil® |
| LEXAN™ LGK4010 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| LEXAN™ EXL1434 resin | SABIC Innovative Plastics | PC | LEXAN™ |