MAGNUM™ 3325 SLG
| Category: | ABS , ABS Resin |
| Manufacturer: | Trinseo |
| Trademark: | MAGNUM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ASKgGW_MAGNUM-3325-SLG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Super Low Gloss, Medium Heat, Medium Impact ABS resin for injection molded automotive interior trim applications. Magnum 3325 SLG can achieve 60 degree Gardner gloss levels below 2.0 with low gloss gradient across the molded part. Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792, ISO 1183/B |
| Apparent Density | 0.69 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 3.1 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.53 | % | |
| Flow | 0.52 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2080 | MPa | ASTM D638 |
| -- | 1920 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield 2 | 40.0 | MPa | ASTM D638 |
| Yield | 37.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 3 | 2.8 | % | ASTM D638 |
| Yield | 2.8 | % | ISO 527-2/50 |
| Break 4 | 22 | % | ASTM D638 |
| Break | 19 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2140 | MPa | ASTM D790 |
| -- | 2070 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 6 | 64.1 | MPa | ASTM D790 |
| -- | 61.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 11 | kJ/m² | |
| 23°C | 16 | kJ/m² | |
| Notched Izod Impact | |||
| -30°C | 130 | J/m | ASTM D256 |
| 23°C | 190 | J/m | ASTM D256 |
| -30°C | 11 | kJ/m² | ISO 180/A |
| 23°C | 18 | kJ/m² | ISO 180/A |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Peak Energy | 23.0 | J | |
| 23°C, Peak Energy | 30.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 96.7 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 97.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 82.2 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 82.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 101 | °C | ISO 306/B50, ASTM D1525 7 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 100°C | 8.3E-5 | cm/cm/°C | |
| Transverse : -40 to 100°C | 9.0E-5 | cm/cm/°C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| FMVSS Flammability 8 | 24 | mm/min | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.0 to 85.0 | °C | |
| Drying Time | > 2.0 | hr | |
| Rear Temperature | 238 | °C | |
| Middle Temperature | 249 | °C | |
| Front Temperature | 254 | °C | |
| Nozzle Temperature | 249 to 254 | °C | |
| Processing (Melt) Temp | 243 to 271 | °C | |
| Mold Temperature | 38.0 to 66.0 | °C |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | 51 mm/min |
| 5 . | Method I (3 point load), 1.3 mm/min |
| 6 . | Method I (3 point load), 1.3 mm/min |
| 7 . | Rate A (50°C/h), Loading 2 (50 N) |
| 8 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Promyde® B241 HS | NUREL, S.A. | Nylon 6 | Promyde® |
| Telcar® TL-1050-75 | Teknor Apex Company | TPE | Telcar® |
| Unichem 9812-10 | Colorite Polymers | PVC, Unspecified | Unichem |
| Kepamid® 1345GF | Korea Engineering Plastics Co., Ltd | Nylon 6 | Kepamid® |
| ISOTHANE® 2080A | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyester | ISOTHANE® |