Petro Rabigh PP FS2011E
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Rabigh Refining & Petrochemical Co. |
| Trademark: | Petro Rabigh PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AS6gc1_Petro-Rabigh-PP-FS2011E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FS2011E is a homopolymer polypropylene intended for the extrusion of biaxially oriented film. It is easy to process and metallization. The film made from this resin exhibit excellent transparency, excellent mechanical and barrier properties. Applications
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.2 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | 98 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 32.0 | MPa | ASTM D638 |
| Fracture | 19.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 9.0 | % | ASTM D638 |
| Fracture | 160 | % | ASTM D638 |
| Flexural Modulus | 1280 | MPa | ASTM D790 |
| Flexural Strength | 34.0 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 20 µm | 2050 | MPa | ASTM D882 |
| 1% secant, TD : 20 µm | 3700 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 20 µm | 110 | MPa | ASTM D882 |
| TD : Break, 20 µm | 215 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 20 µm | 85 | % | ASTM D882 |
| TD : Break, 20 µm | 17 | % | ASTM D882 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 2.9 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 153 | °C | ASTM D1525 1 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss 2(45°, 20.0 µm) | 155 | ASTM D2457 | |
| Haze 3(20.0 µm) | 0.20 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 250 | °C |
| Extrusion instructions |
|---|
| Stretching Temperature: 130 to 160°CStretching Ratio MD/TD: 4 to 7 / 7 to 10 |
| Note Message | |
|---|---|
| 1 . | 压 力1 (10N) |
| 2 . | Film |
| 3 . | Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MALEX 01EN002 - 6208 | AD majoris | PC | MALEX |
| RTP 600 UV | RTP Company | ABS | RTP |
| RTP 301 HF UV | RTP Company | PC | RTP |
| apigo® 8376 BS/55 | API SpA | TPO (POE) | apigo® |
| Hostacom HKC 465T | LyondellBasell Industries | PP Homopolymer | Hostacom |