TEKAPPO™ JF2
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | TEKAPPO™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ARwG8B_TEKAPPO-JF2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| JF2 is PPO/PS unreinforced product and heat resistant chemical resistance product. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 - 0.70 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.060 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 71.6 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 30 | % | ASTM D638 |
| Flexural Modulus 3 | 2650 | MPa | ASTM D790 |
| Flexural Strength 4 | 113 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 150 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 145 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 270 - 310 | °C | |
| Middle Temperature | 270 - 310 | °C | |
| Front Temperature | 270 - 310 | °C | |
| Nozzle Temperature | 280 - 320 | °C | |
| Processing (Melt) Temp | 280 - 310 | °C | |
| Mold Temperature | 60.0 - 100 | °C |
| Injection instructions |
|---|
| Injection Speed: 30 to 70%Injection Pressure - 1st: 20 to 50%Injection Pressure - 2nd: 20 to 50%Injection Pressure - Back Pressure: 0 to 20% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 3.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx 80S7150 | The Matrixx Group, Inc. | PET | Matrixx |
| Sinvicomp SFC4506 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Argothane® 19426 | Argotec LLC | TPU, Unspecified | Argothane® |
| Hostacom HKC 465T BLACK | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Dryflex® SE 35A201 | ELASTO | TPE | Dryflex® |