HAIPLEN EP10 G6 BA
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | HAIPLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ARvNlm_HAIPLEN-EP10-G6-BA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene copolymer 30% glass fibres reinforced chemically coupled, medium low flow. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 0.70 - 0.90 | % | Internal method |
| Flow direction | 0.20 - 0.40 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4900 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 85.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 5.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 4700 | MPa | ISO 178 |
| Flexural Stress 2 | 105 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 170 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 127 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 147 | °C | ISO 306/A50 |
| -- | 120 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Oxygen Index | 20 | % | ASTM D2863 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content 3(600°C) | 30 | % | ISO 3451 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 210 - 240 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Pre-heat Temperature: 70 to 80°CPre-heat Time: 3 hr |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 1.0 mm/min |
| 3 . | 1 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Clearflex® MP D0 | Versalis S.p.A. | VLDPE | Clearflex® |
| FireCon™ CPE 30-11 RoHS BLACK | PolyOne Corporation | CPE | FireCon™ |
| Geon™ BIO RA7000 | PolyOne Corporation | PVC, Flexible | Geon™ BIO |
| Kumho SSBR SOL-5150 | Korea Kumho Petrochemical Co., Ltd. | SBR, Solution | Kumho SSBR |
| TOTAL Polyethylene Bio TPSeal® 0750_03 | TOTAL Refining & Chemicals | mPE | TOTAL Polyethylene |