Radilon® A RV500RW 339 NER 5398
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Radici Plastics |
| Trademark: | Radilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ARhz0e_Radilon-A-RV500RW-339-NER-5398.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA66 50% glass fiber reinforced injection moulding grade. Heat stabilized. Deep black colour. Suitable for technical parts requiring very high stiffness and high mechanical resistance. Excellent heat ageing properties retention, improved welding lines strength. Especially fit for demanding metal replacement applications. ISO 1043 : PA66-T GF50 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.58 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C, 2.00 mm | 4.0 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 1.2 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 17500 | -- | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 250 | -- | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.8 | -- | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 16200 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 385 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 100 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 255 | -- | °C | ISO 75-2/Af |
| Melting Temperature 3 | 260 | -- | °C | ISO 11357 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | 0.0 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.00 mm | 700 | -- | °C | |
| 2.00 mm | 700 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 1.00 mm | 725 | -- | °C | |
| 2.00 mm | 725 | -- | °C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
| Dew Point - Desiccant Dryer | < -20.0 | °C | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ULTEM™ 2312EPR resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| ALTECH® PA66 A 1000/501 IM | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| Lifoflex® UV 90 GC 1090 | ELASTO | SEBS | Lifoflex® |
| PENTAMID A GV25 H RC schwarz | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |
| Tribocomp® PA612 CF30 TS12 | Solvay Specialty Polymers | Nylon 612 | Tribocomp® |