LNP™ KONDUIT™ PX11311 compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ KONDUIT™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ARfDhA_LNPKONDUITPX11311compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Thermally conductive mineral and glass fiber filled PA6 Eco-FR compound Also known as: LNP* KONDUIT* Compound PX11311 Product reorder name: PX11311 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.76 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 102 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.5 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 11000 | MPa | ISO 178 |
| Flexural Stress | 164 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(23°C) | 3.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 22 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 64.0 mm Span) | 185 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 208 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 3.1E-5 | cm/cm/°C | ASTM E831 |
| Flow : -30 to 80°C | 3.5E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 23 to 80°C | 3.7E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 4.8E-5 | cm/cm/°C | ASTM E831 |
| Horizontal : -30 to 80°C | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 7.3E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | ISO 22007-2 | ||
| -- 5 | 1.1 | W/m/K | ISO 22007-2 |
| -- 6 | 1.3 | W/m/K | ISO 22007-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.00 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 260 - 275 | °C | |
| Middle Temperature | 270 - 290 | °C | |
| Front Temperature | 270 - 290 | °C | |
| Processing (Melt) Temp | 270 - 295 | °C | |
| Mold Temperature | 85.0 - 100 | °C | |
| Back Pressure | 0.200 - 0.300 | MPa | |
| Screw Speed | 20 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | through-plane, ø80*3mm discs |
| 6 . | in-plane, ø80*3mm discs |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 511A | Saudi Basic Industries Corporation (SABIC) | PP Homopolymer | SABIC® PP |
| VITAMIDE® BS10VN6551 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Daelim Po1y® PH-630 | DAELIM INDUSTRIAL CO., LTD. | PP Homopolymer | Daelim Po1y® |
| Hostacom BB 1161 F M 2689 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Lupolen 5461 B Q 471 | LyondellBasell Industries | HDPE | Lupolen |