OnForce™ LFT LF0100-5004 X2 BLACK

Category:	PUR, Unspecified , Polyurethane
Manufacturer:	PolyOne Corporation
Trademark:	OnForce™ LFT
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	AR2HYG_OnForceLFTLF01005004X2BLACK.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
PolyOne's Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. These products exhibit enhanced physical and mechanical properties versus standard short fiber products. Benefits of LFT compounds include improved impact strength, elastic modulus, and material strength across wide temperature ranges from subambient to highly elevated. Furthermore, LFT compounds have been shown to offer improved performance in the areas of creep and fatigue performance, improved dimensional stability, and exhibit an exceptional surface finish when compared to traditional highly filled short fiber products.

General Information
Filler / Reinforcement	Long carbon fiber, 20% filler by weight
Forms	Particle

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.27	g/cm³	ISO 1183
Molding Shrinkage - Flow	0.10 - 0.20	%	ISO 294-4

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus ¹	15400	MPa	ISO 527-2
Tensile Strength (Yield)	205	MPa	ISO 527-2
Tensile Elongation ²(Break)	2.0	%	ISO 527-2
Flexural Modulus	12000	MPa	ISO 178
Flexural Strength (Yield)	270	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength	16	kJ/m²	ISO 179
Charpy Unnotched Impact Strength	45	kJ/m²	ISO 179
Dart Drop Impact	15.6	J	ASTM D5420

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	110	°C	ISO 75-2/A

Injection	Nominal Value	Unit
Drying Temperature	90	°C
Drying Time	8.0 - 12	hr
Processing (Melt) Temp	220 - 250	°C
Mold Temperature	80	°C

Injection instructions
LFT compounds can be processed using equipment similar to that used for short fiber products. The mechanical properties of finished parts dependgreatly on the length of the fibers in the molded part; therefore processing conditions must be set carefully in order to minimize fiber breakage. A "lowshear process" is advised, with low back pressure, low screw speed and low-to-medium injection speed.This grade must be dried in a dessicant dryer with a dew point set at -40°C.

Injection instructions

LFT compounds can be processed using equipment similar to that used for short fiber products. The mechanical properties of finished parts dependgreatly on the length of the fibers in the molded part; therefore processing conditions must be set carefully in order to minimize fiber breakage. A "lowshear process" is advised, with low back pressure, low screw speed and low-to-medium injection speed.This grade must be dried in a dessicant dryer with a dew point set at -40°C.

Note Message
1 .	Type 1, 5.1 mm/min
2 .	Type 1, 5.1 mm/min

Resin Grade	Manufacturer	Category	Trademark
Radilon® AGV 20 Natural	Radici Plastics	Nylon 66	Radilon®
Santoprene™ 241-80W236	ExxonMobil Chemical	TPV	Santoprene™
WPP PP M2956-002	Washington Penn Plastic Co. Inc.	PP, Unspecified	WPP PP
UNITHENE® LH503	USI Corporation	HDPE	UNITHENE®
Kazan HDPE 293-2B5D	Kazanorgsintez Joint Stock Company	HDPE	Kazan HDPE