Order Products : sales@su-jiao.com
LubX® S pressed
| Category: | UHMWPE , Ultra High Molecular Weight Polyethylene |
| Manufacturer: | Röchling Engineering Plastics SE & Co. KG |
| Trademark: | LubX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AQp2Mq_LubX-S-pressed.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Product characteristics
Typical field of application
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.930 | g/cm³ | ISO 1183 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | < 0.010 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 60 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 650 | MPa | ISO 527-2/1B/1 |
| Tensile Stress (Yield) | 20.0 | MPa | ISO 527-2/1B/50 |
| Tensile Strain | |||
| Yield | 14 | % | ISO 527-2/1B/50 |
| Fracture | > 50 | % | ISO 527-2 |
| Wear Resistance - Sand-slurry method | 90.0 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Material Designation | UHMW-PE-QCD 35-3-4 | ISO 1872 | |
| Use- Sliding properties: partner PET | 0.100 | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | No Break | ISO 179 | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -- 1 | 100 | kJ/m² | ISO 179 |
| -- | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Continuous Use Temperature 2 | < 130 | °C | |
| Melting Temperature 3 | 133 - 135 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | DIN VDE 0303 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | DIN VDE 0303 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 3.00 mm | HB | UL 94 | |
| 6.00 mm | HB | UL 94 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Service Temperature (Long Term): -150 to 80°C |
| Note Message | |
|---|---|
| 1 . | 15° Notch |
| 2 . | Short Term |
| 3 . | Crystalline grain |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® GFX1743-BK1(PTFE) | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| ExxonMobil™ PP1364E2 | ExxonMobil Chemical | PP Homopolymer | ExxonMobil™ |
| Hax™ HFC 0115/1 | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |
| Lupoy® GN2301F | LG Chem Ltd. | PC | Lupoy® |
| Plaslube® PEEK CF15 TL15 A | Techmer Engineered Solutions | PEEK | Plaslube® |