LNP™ LUBRICOMP™ KN001 compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AQb9zz_LNP-LUBRICOMP-KN001-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP KN001 is a compound based on POM resin containing MOS2. Also known as: LNP* LUBRICOMP* Compound KN001 Product reorder name: KN001 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 2.0 to 2.8 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.21 | % | |
| Equilibrium, 23°C, 50% RH | 0.030 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2870 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 59.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 9.2 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 2840 | MPa | ISO 178 |
| Flexural Stress | 88.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.42 | ||
| vs. Itself - Static | 0.70 | ||
| Wear Factor - Washer | 122 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 4.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 50 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 150 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 83.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 145 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.3E-4 | cm/cm/°C | |
| Transverse : 23 to 60°C | 1.3E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Processing (Melt) Temp | 199 to 216 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Siloxane Masterbatch MB50-010 | Multibase, A Dow Corning Company | Siloxane, UHMW | Siloxane Masterbatch |
| DENKA POVAL H-24 | Denka Company Limited | PVOH | DENKA POVAL |
| Hyosung Polyketone M630A | Hyosung Corporation | PK-Aliphatic | Hyosung Polyketone |
| Polifor® L6 GF/30 H-D-R NATURALE | SO.F.TER. SPA | PP Homopolymer | Polifor® |
| Makrolon® Solid Sheet GP | Covestro - Polycarbonates | PC | Makrolon® Solid Sheet |