Aplax P0050FN
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Ginar Technology Co., LTD. |
| Trademark: | Aplax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AQWg2I_Aplax-P0050FN.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame Retardant , Halogen |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.958 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (1.60 mm) | 1.7 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.010 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 34.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 30 | % | ASTM D638 |
| Flexural Modulus | 1450 | MPa | ASTM D790 |
| Flexural Strength | 48.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 37 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 125 | °C | ASTM D648 |
| Melting Temperature | 165 | °C | ASTM D789 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.794 mm | V-0 | ||
| 1.59 mm | V-0 | ||
| 3.18 mm | V-0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vinnolit® K 221 | Vinnolit GmbH & Co. KG | PVC, Unspecified | Vinnolit® |
| Ultramid® A3HG5 | BASF Corporation | Nylon 66 | Ultramid® |
| VALOX™ 4012G resin | SABIC Innovative Plastics Europe | PBT | VALOX™ |
| LNP™ STAT-KON™ RX05489 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ STAT-KON™ |
| DAI-EL™ G-101 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |