EMAREX® 300
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | MRC Polymers, Inc. |
| Trademark: | EMAREX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AQ8ifG_EMAREX-300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Further information and details are available upon request.
|
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.2 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.6 | % | ASTM D570 |
| Relative Viscosity | 50 | mPa·s | ASTM D789 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 79.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 70 | % | ASTM D638 |
| Flexural Modulus | 2690 | MPa | ASTM D790 |
| Flexural Strength | 108 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 160 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 63.9 | °C | ASTM D648 |
| Melting Temperature | 215 | °C | ASTM D789 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 93.3 | °C | |
| Dew Point | < -17.8 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 243 - 254 | °C | |
| Middle Temperature | 249 - 260 | °C | |
| Front Temperature | 254 - 266 | °C | |
| Nozzle Temperature | 254 - 271 | °C | |
| Processing (Melt) Temp | 254 - 271 | °C | |
| Mold Temperature | 37.8 - 82.2 | °C | |
| Injection Pressure | 68.9 - 138 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.345 - 1.21 | MPa | |
| Screw Speed | 50 - 75 | rpm | |
| Cushion | 6.35 | mm |
| Injection instructions |
|---|
| Packing: 50 to 75% of injection pressureHold: 40 to 60% of injection pressureAir Flow Rate: 0.8-1.0 CFM per lb/hour resin processed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3908T | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| RANPELEN J-560K | Lotte Chemical Corporation | PP Random Copolymer | RANPELEN |
| TECHNYL® eXten D 218 V30 BLACK | Solvay Engineering Plastics | Nylon 610 | TECHNYL® eXten |
| Spectrum S670 | Spartech Plastics | HDPE | Spectrum |
| CoREZYN® COR45-BA-199 | Interplastic Corporation | Vinyl Ester | CoREZYN® |