UV stabilised silane crosslinkable polyethylene compound for "Câble Torsadé" overhead power cable insulation This is a chemically crosslinkable polyethylene compounds for insulation of cables where resistance to ultra-violet radiation is required. The material is carbon loaded and possesses excellent extrusion properties at high output rates. The graft component SX523 is mixed with a crosslinking catalyst masterbatch CM493 or CM497 generally in the ratio 95:5 and is curable by exposure to moist conditions. The compound has been specially developed for the "Câble Torsadé" NFC 33-209 specification for overhead power cable applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.950 | g/cm³ | BS 2782 620A |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 18.0 | MPa | IEC 60811-1-1 |
| Tensile Strain (Break) | 450 | % | IEC 60811-1-1 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength (150°C, 240 hr) | 20 | % | IEC 60811-1-2 |
| Change in Tensile Strain at Break (150°C, 240 hr) | -18 | % | IEC 60811-1-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset 1 | IEC 60811-2-1 | ||
| Elongation under load, 20N/cm² : 200°C | 80 | % | IEC 60811-2-1 |
| Permanent elongation after cooling | 5.0 | % | IEC 60811-2-1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Power factor- 50Hz (23°C) | 0.00170 | IEC 60250 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 200 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (20°C) | > 1.5E+16 | ohms·cm | IEC 60502 |
| Relative Permittivity (23°C, 50 Hz) | 3.47 | IEC 60250 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 130 | °C | |
| Cylinder Zone 2 Temp. | 150 | °C | |
| Cylinder Zone 3 Temp. | 170 | °C | |
| Cylinder Zone 4 Temp. | 190 | °C | |
| Die Temperature | 210 | °C |
| Extrusion instructions |
|---|
| Most modern thermoplastic extruders will process SX523:CM493 compounds, particularly if a screw suitable for polyethylene extrusion is available. |
| Note Message | |
|---|---|
| 1 . | Cure assessment by hot set test (forced cured at 80°C in water) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYshine PBT D231 GF30 | Polykemi AB | PBT | POLYshine |
| Resinoid 2017 | Resinoid Engineering Corporation | Phenolic | Resinoid |
| Kumho PS GP 150I | Korea Kumho Petrochemical Co., Ltd. | PS (GPPS) | Kumho PS |
| Karina WHITE PVC COMPOUND 807-10/236-H-ISE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| ULTEM™ 4001 resin | SABIC Innovative Plastics | PEI | ULTEM™ |