Order Products : sales@su-jiao.com
NILENE® P K30VA S
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | NILENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | APH0mn_NILENE-P-K30VA-S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene homopolymer 30% glass fibres reinforced chemically coupled, heat stabilized, good mechanical properties, flame rating UL94 HB. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 0.70 - 0.90 | % | Internal method |
| Flow direction | 0.20 - 0.40 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 90.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 3.5 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 5700 | MPa | ISO 178 |
| Flexural Stress 2 | 125 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 70 | J/m | ASTM D256 |
| 23°C | 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 155 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 142 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 155 | °C | ISO 306/A50 |
| -- | 133 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 3(2.00 mm) | < 100 | mm/min | ISO 3795 |
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | UL 94 | |
| 1.50 mm | HB | UL 94 | |
| Oxygen Index | 20 | % | ASTM D2863 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content | 30 | % | ISO 3451 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 220 - 250 | °C | |
| Mold Temperature | 50.0 - 70.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Pre-heat Temperature: 70 to 80°CPre-heat Time: 1 hr |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 1.0 mm/min |
| 3 . | US FMVSS302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BMC 605LWR | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Ferro PP TPP20AR14WH | Ferro Corporation | PP Copolymer | Ferro PP |
| Hifax TRS 260P BLACK | LyondellBasell Industries | TPO (POE) | Hifax |
| Hyundai EP PA66 LD340 | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |
| Sylvin 9302-75 FU WHITE 1279 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |