NORYL™ WCD883AU resin
| Category: | PPE+TPE , Polyphenylene Ether + TPE |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AOOxDI_NORYLWCD883AUresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Flexible and non-halogenated flame retardant extrusion grade intended for evaluation in applications such as jacket of HD 21.14 flexible cables. Flame retardant performance capable of meeting EN 50265-2-1 requirement. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 4.0 | g/10 min | ASTM D1238 |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 30 sec) | < 87 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Fracture | 18.0 | MPa | UL 1581 |
| Fracture 1 | 14.0 | MPa | ASTM D638 |
| Fracture, 136°C 2 | 19.0 | MPa | UL 1581 |
| Fracture | 15.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture | 260 | % | UL 1581 |
| Fracture 3 | 260 | % | ASTM D638 |
| Fracture, 136°C 4 | 240 | % | UL 1581 |
| Fracture | 240 | % | ISO 527-2/50 |
| Flexural Modulus 5 | |||
| 100mm span | 37.0 | MPa | ASTM D790 |
| -- | 45.0 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deformation (100°C) 6 | 23 | % | UL 1581 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vertical Flame Test | PASSES | EN 50265-2-1 | |
| Smoke Density | ASTM E662 | ||
| Flame, 0.5 mm plaque, Ds, max | 57 | ASTM E662 | |
| Non-Flame, 0.5 mm plaque, Ds, max | 140 | ASTM E662 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.5E+16 | ohms | ASTM D257 |
| Volume Resistivity | 5.6E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm, in Oil) | 25 | kV/mm | ASTM D149 |
| Dielectric Constant (1.00 GHz) | 3.00 | ASTM D150 | |
| Dissipation Factor (1.00 GHz) | 3.0E-3 | ASTM D150 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (3.0 mm) | 850 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (3.0 mm) | 775 | °C | IEC 60695-2-13 |
| Oxygen Index | 36 | % | ISO 4589-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75 - 85 | °C | |
| Drying Time | 5.0 - 7.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Cylinder Zone 1 Temp. | 180 - 220 | °C | |
| Cylinder Zone 3 Temp. | 220 - 250 | °C | |
| Cylinder Zone 5 Temp. | 220 - 250 | °C | |
| Melt Temperature | 220 - 250 | °C | |
| Die Temperature | 220 - 250 | °C |
| Extrusion instructions |
|---|
| Conductor Pre-heat Temperature: 25 - 120 °CCooling Water Air Gap: 100 - 200 mmCross-head Temperature: 220 - 250 °CDrying Time (Cumulative): 12 hrsExtruder Length/Diameter Ratio (L/D): 22:1 to 26:1Neck Temperature: 220 - 250 °CScreen Pack: 150 - 100Screw Speed: 15 - 85 rpmWater Bath Temperature: 15 - 60 °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 50mm/min |
| 2 . | After 7 days |
| 3 . | Type 1, 50mm/min |
| 4 . | After 7 days |
| 5 . | 13 mm/min |
| 6 . | 250 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1099 X 117938 B | RTP Company | PBT | RTP |
| STERLENE™ BMU147 | R&P (Pte.) Ltd. | TPO (POE) | STERLENE™ |
| Karina BLACK PVC COMPOUND -E 753D48/ 1-C-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina GRAY PVC COMPOUND 751-18/126-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ YL003 compound | SABIC Innovative Plastics | TPEE | LNP™ LUBRICOMP™ |