MonoSol® M8900
| Category: | PVOH , Polyvinyl Alcohol |
| Manufacturer: | MonoSol, LLC |
| Trademark: | MonoSol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AO4g4U_MonoSol-M8900.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MonoSol M8900 is a PVOH based thermoplastic film, soluble in cold water and manufactured using MonoSol's proprietary solution cast technology. MonoSol M8900 film has been engineered specifically to be resistant to both alkaline and acidic hydrolysis. Coupled with its exceptional cold water solubility, M8900 is an excellent candidiate for detergent and disinfectant unit dose packaging. M8900 offers superior resistance to boron-containingcompounds and can be easily converted on all conventionalpackaging machines. Standard thicknesses are 38 micron (1.5 mil), 51 micron (2.0 mil) and 76 micron (3.0 mil). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Moisture Content (23°C) 1 | 4.4 | wt% | |
| Solubility 2 | |||
| Disintegration : 10°C, 76.2 µm | 31.0 | sec | |
| Dissolution : 10°C, 76.2 µm | 56.0 | sec |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yield (76.2 µm) | 9.96 | m²/kg | ASTM D4321 |
| Film Thickness - Tested | 76 | µm | |
| Film Thickness - Recommended / Available | 38 µm, 51 µm, and 76 µm | ||
| Secant Modulus - 100%, MD | 10.3 | MPa | ASTM D882, ISO 527-3 |
| Tensile Strength - MD | |||
| Break | 27.6 | MPa | ASTM D882 |
| -- | 27.6 | MPa | ISO 527-3 |
| Tensile Elongation - MD (Break) | 440 | % | ASTM D882, ISO 527-3 |
| Dart Drop Impact | 1200 | g | ASTM D1709, DIN 53433 |
| Elmendorf Tear Strength - MD | |||
| -- | 760 | g | ASTM D1922 |
| -- | 0.077 | N | ISO 6383-2 |
| Note Message | |
|---|---|
| 1 . | 50%RH |
| 2 . | Distilled Water (MSTM 205) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rhelon F2038H-01 | RheTech, Inc. | Nylon 66 | Rhelon |
| Bergamid™ B700 G15 H | PolyOne Corporation | Nylon 6 | Bergamid™ |
| ASI POLYPROPYLENE 1277E-01 | A. Schulman Inc. | PP Impact Copolymer | ASI POLYPROPYLENE |
| Elastron® G G400.A05.B | Elastron USA, Inc. | SEBS | Elastron® G |
| MARPOL® HDM 504-RC | Marco Polo International, Inc. | HDPE | MARPOL® |