Telcar® TL-3260R
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Telcar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ANkd37_Telcar-TL-3260R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Telcar®TL-3260R is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is extrusion or injection molding. Telcar®The main features of the TL-3260R are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.86 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw D, 1 sec | 56 | ASTM D2240 | |
| Shaw D, 5 seconds | 51 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| Transverse flow : 100% strain | 7.14 | MPa | ASTM D412 |
| Flow : 100% strain | 10.7 | MPa | ASTM D412 |
| Tensile Strength | ASTM D412 | ||
| Transverse flow : Fracture | 11.0 | MPa | ASTM D412 |
| Flow : Fracture | 10.7 | MPa | ASTM D412 |
| Tensile Elongation | ASTM D412 | ||
| Transverse flow : Fracture | 660 | % | ASTM D412 |
| Flow : Fracture | 240 | % | ASTM D412 |
| Tear Strength - Across Flow | 80.0 | kN/m | ASTM D624 |
| Compression Set | ASTM D395 | ||
| 23°C, 22 hr | 47 | % | ASTM D395 |
| 70°C, 22 hr | 86 | % | ASTM D395 |
| 90°C, 70 hr | 97 | % | ASTM D395 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air | ISO 188 | ||
| 110°C, 1008 hr | -0.30 | % | ISO 188 |
| 125°C, 168 hr | 2.9 | % | ISO 188 |
| Change in Tensile Strain at Break in Air | ISO 188 | ||
| 110°C, 1008 hr | -0.30 | % | ISO 188 |
| 125°C, 168 hr | 2.9 | % | ISO 188 |
| Change in Shore Hardness in Air (110°C, 1008 hr) | 2.3 | ISO 188 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -68.0 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 28 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 2.32 | ASTM D150 | |
| 1 MHz | 2.33 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 1 kHz | 4.0E-4 | ASTM D150 | |
| 1 MHz | 2.0E-4 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 | |
| Oxygen Index | 24 | % | ASTM D2863 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Viscosity (200°C, 206 sec^-1) | 701 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 171 - 193 | °C | |
| Middle Temperature | 177 - 199 | °C | |
| Front Temperature | 182 - 204 | °C | |
| Nozzle Temperature | 188 - 210 | °C | |
| Processing (Melt) Temp | 188 - 210 | °C | |
| Mold Temperature | 25.0 - 65.6 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.172 - 0.345 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C). |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Cylinder Zone 1 Temp. | 166 - 188 | °C | |
| Cylinder Zone 2 Temp. | 171 - 193 | °C | |
| Cylinder Zone 3 Temp. | 177 - 199 | °C | |
| Cylinder Zone 5 Temp. | 182 - 204 | °C | |
| Die Temperature | 190 - 210 | °C |
| Extrusion instructions |
|---|
| 螺杆转速30 - 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILVER® FC-2 | Guangdong Silver Age Sci & Tech. Co., Ltd | PVC, Unspecified | SILVER® |
| Vydyne® 66R | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Zhongfa PA66 ST-24 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | Nylon 66 | Zhongfa |
| EVERLON® TP-38D | Ever Polymer Co., Ltd. | SEBS | EVERLON® |
| Sylvin 2900-80 Clear White 1504 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |