POLYLAC® PA-709P
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | CHI MEI CORPORATION |
| Trademark: | POLYLAC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ANRWtg_POLYLAC-PA-709P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLYLAC® PA-709P is an Acrylonitrile Butadiene Styrene (ABS) product. It can be processed by extrusion and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.03 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 8.50 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 86.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 45.0 | MPa | |
| Break | 36.0 | MPa | |
| Tensile Strain (Break) | 60 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1900 | MPa | ISO 178 |
| Flexural Stress 2 | 58.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 27 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | No Break | ISO 179 | |
| Notched Izod Impact Strength | 27 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | ISO 75-2/A | ||
| 1.8 MPa, Unannealed | 80.0 | °C | |
| 1.8 MPa, Annealed | 98.0 | °C | |
| Vicat Softening Temperature | |||
| -- | 103 | °C | ISO 306/A50 |
| -- | 95.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Cylinder Zone 1 Temp. | 190 to 210 | °C | |
| Cylinder Zone 3 Temp. | 210 to 240 | °C | |
| Cylinder Zone 5 Temp. | 220 to 250 | °C | |
| Die Temperature | 200 to 250 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ F-300SP | Prime Polymer Co., Ltd. | PP Homopolymer | Prime Polypro™ |
| SABIC® PP 513A | Saudi Basic Industries Corporation (SABIC) | PP Homopolymer | SABIC® PP |
| Andur AL 70 DP | Anderson Development Company | PUR-Eth,aliphat | Andur |
| MAJ'ECO CEP204EW | AD majoris | PE, Unspecified | MAJ'ECO |
| Hostacom PPU X9067HS 305514 | LyondellBasell Industries | PP Copolymer | Hostacom |