Eltex® P KS414
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | Eltex® P |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ANQslg_Eltex-P-KS414.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Benefits & Features Eltex® P KS414 is a random copolymer with a high ethylene content, developed for use primarily as the sealing layer in "coextruded bioriented film". It contains slip and anti-blocking agents. Applications
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.895 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.3 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 23°C) | 62 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 21.0 | MPa | ISO 527-2 |
| Flexural Modulus (23°C) | 750 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Seal Threshold 1 | 115 | °C | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 60.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 120 | °C | ISO 306/A50 |
| Peak Melting Temperature | 134 | °C | ASTM D3417 |
| Note Message | |
|---|---|
| 1 . | 1s, 3 bars, 100 mm/min, 100 g/cm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren DJ210 (On-spec.) | SINOPEC Shanghai Petrochemical Co. Ltd. | LDPE | Sanren |
| SOLPLAST TC 3000B | UTEKSOL d.o.o. | SBS | SOLPLAST TC |
| SolVin 178GI | INOVYN | PVC, Unspecified | SolVin |
| ALCUDIA® LDPE 1970M | REPSOL | LDPE | ALCUDIA® LDPE |
| Hifax PPU 1752S2S003 | LyondellBasell Industries | PP Copolymer | Hifax |