LNP™ THERMOTUF™ VF004S compound
| Category: | Nylon, Unspecified , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOTUF™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AMtDcP_LNPTHERMOTUFVF004Scompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOTUF VF004S is a compound based on Super Tough Nylon resin containing Glass Fiber. Added features of this material include: Heat Stabilized. Also known as: LNP* THERMOTUF* Compound VF-1004 HS Product reorder name: VF004S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.30 - 0.60 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.70 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5800 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 94.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.5 | % | ISO 527-2/5 |
| Flexural Stress 1 | ISO 178 | ||
| -- 2 | 4500 | MPa | ISO 178 |
| -- 3 | 134 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 4(23°C) | 22 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 5(23°C) | 55 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6 | |||
| 0.45 MPa, unannealed, 64.0mm span | 248 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 235 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 3.8E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 1.7E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 260 - 271 | °C | |
| Middle Temperature | 277 - 288 | °C | |
| Front Temperature | 293 - 304 | °C | |
| Processing (Melt) Temp | 282 - 293 | °C | |
| Mold Temperature | 93.3 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | Break |
| 3 . | Yield |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V976 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Sindustris PBT LW5103F | Sincerity Australia Pty Ltd. | PC+PBT | Sindustris PBT |
| Somos® NeXt | DSM Somos® | Unspecified | Somos® |
| Toyolac® 470Y-TG1 | Toray Resin Company | ABS | Toyolac® |
| KMI PE KM-3416CDMD | KMI Group, Inc. | HDPE | KMI PE |