Baytec® EDG-085A
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Covestro - PUR |
| Trademark: | Baytec® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AKK08O_Baytec-EDG-085A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Baytec EDG-085A is a two-component, one-shot system which yields a solid polyurethane elastomer. It is a UV-stable system with an approximate hardness of 85 Shore A. The isocyanate component is an aliphatic, HDI-based polyisocyanate, and the polyol component is a polyether/polyester polyol blend. The Baytec EDG-085A system is used in table-edging applications. As with any product, use of the Baytec EDG-085A system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore D) | 85 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance (1000 Cycles) | 149 | mg | ASTM D4066 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 8.27 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 100 | % | ASTM D412 |
| Tear Strength | |||
| -- 1 | 18.9 | kN/m | ASTM D624 |
| Cracking | 5.8 | kN/m | ASTM D1938 |
| Thermoset | Nominal Value | ||
|---|---|---|---|
| Thermoset Components 2 | |||
| Component a | Mixing ratio by weight: 91 | ||
| Component B | Mixing ratio by weight: 100 |
| Additional Information |
|---|
| Part A Type: Isocyanate Appearance: Clear, pale yellow liquid Specific Gravity @ 25°C: 1.17 Viscosity @25°C: 2900 mPa Flash Point, SETA: 238°C NCO: 21.5 wt% Part B Type: Polyol Appearance: Clear, viscous liquid Specific Gravity @ 25°C: 1.06 Viscosity @25°C: 2500 mPa-s Flash Point, PMCC: 146°C Water: 0.08 wt% max Hydroxyl Number: 250 mg KOH/g IsocyanateTemperature: 41 to 46°CPolyol Temperature: 32 to 44°CMold Temperature: 44 to 60°CGel Time: 75 to 120 secDemold Time: 6 to 15 min |
| Note Message | |
|---|---|
| 1 . | C mould |
| 2 . | 105 Index |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALLOY® A1700 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | PRIMALLOY® |
| Synthos EPS® 0308F/PL | Synthos S.A. | PS (EPS) | Synthos EPS® |
| NEFTEKHIM PP 1452R (Z69S) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| Nypol® PA A3 G25 PRTA011 NR306 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Sylvin 3270-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |