Zytel® ST801AW BK195
| Category: | Nylon 66 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AK9zFM_ZytelST801AWBK195.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Super Toughened, UV Stabilized, Polyamide 66 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.09 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 1.4 | -- | % | ISO 294-4 |
| Flow | 1.8 | -- | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 1.1 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 1900 | 1240 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | |||
| Yield | 47.0 | -- | MPa | ISO 527-2 |
| 50% strain | -- | 41.0 | MPa | ISO 527-2 |
| Tensile Strain | ||||
| Yield | 30 | -- | % | ISO 527-2 |
| Fracture | -- | > 50 | % | ISO 527-2 |
| Fracture, 23°C | 75 | -- | % | ISO 527-2/50 |
| Flexural Modulus | 1800 | 700 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 19 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 79 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | -- | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | |||
| -40°C | 18 | -- | kJ/m² | ISO 180/1A |
| 23°C | 80 | -- | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | No Break | -- | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 162 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 62.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 262 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow | 1.5E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.3E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 3.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | 7.4E+12 | ohms·cm | IEC 60093 |
| Dielectric Strength | 25 | 22 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 3.90 | 6.70 | IEC 60250 | |
| 1 MHz | 3.70 | 4.00 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 6.0E-3 | 0.16 | IEC 60250 | |
| 1 MHz | 0.012 | 0.044 | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 2(1.00 mm) | 26 | -- | mm/min | ISO 3795 |
| Flame Rating | UL 94, IEC 60695-11-10, -20 | |||
| 0.75 mm | HB | -- | UL 94, IEC 60695-11-10, -20 | |
| 1.5 mm | HB | -- | UL 94, IEC 60695-11-10, -20 | |
| FMVSS Flammability | B | -- | FMVSS 302 | |
| Atomization- G-value (condensate) | 1.0E-4 | -- | g | ISO 6452 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Emission of Organic Compounds | 38.4 | -- | µgC/g | VDA 277 |
| Odor | 3.00 | -- | VDA 270 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Melt Temperature, Optimum | 290 | °C | |
| Mold Temperature, Optimum | 80 | °C | |
| Drying Recommended | yes | ||
| Hold Pressure Time | 4.00 | s/mm | |
| Maximum Screw Tangential Speed | 300 | mm/sec |
| Fill Analysis | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ejection Temperature | 190 | -- | °C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time - Desiccant Dryer | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 50 - 100 | °C | |
| Holding Pressure | 50.0 - 100 | MPa |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V859 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Supol HT143E | LyondellBasell Industries | PP Copolymer | Supol |
| Yuyao PPO N100B802 | Yuyao Tenglong Plastics Co., Ltd. | PPE+PS | Yuyao PPO |
| LUVOCOM® 1301-7294/BL | Lehmann & Voss & Co. | PPS | LUVOCOM® |
| LUVOCOM® 1105/MS/15/TF/15 | LEHVOSS Group | PEEK | LUVOCOM® |