RAMSHINE PW300G7
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | RAMSHINE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AIc4SG_RAMSHINE-PW300G7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 35% Glass Fiber reinforced SAN for very high rigidity injection molding applications |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 9.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.20 | % | ASTM D955 |
| -- | 0.20 | % | ISO 2577 |
| Water Absorption | |||
| Saturation | 0.10 | % | ASTM D570 |
| Saturated, 23°C | 0.10 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 94 | ASTM D785 | |
| R scale | 94 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 110 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 1.5 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 10000 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 160 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 65 | J/m | ASTM D256 |
| 23°C | 6.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 110 | °C | ASTM D648, ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+18 | ohms·cm | IEC 60093 |
| Dielectric Strength | 40 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.10 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 220 - 240 | °C | |
| Middle Temperature | 230 - 250 | °C | |
| Front Temperature | 240 - 260 | °C | |
| Processing (Melt) Temp | 240 - 280 | °C | |
| Mold Temperature | 50.0 - 80.0 | °C | |
| Injection Pressure | 70.0 - 105 | MPa | |
| Holding Pressure | 35.0 - 70.0 | MPa | |
| Back Pressure | 0.340 - 0.690 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 25 to 51 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TPV Elastoprene® N67A-E | ELASTORSA Elastomeros Riojanos S.A. | PP+EPDM | TPV Elastoprene® |
| Generic Nylon 4T - Glass Fiber | Generic | Nylon 4T | Generic |
| Kumho KNB 35L | Korea Kumho Petrochemical Co., Ltd. | NBR | Kumho KNB |
| LNP™ THERMOCOMP™ AF001H compound | SABIC Innovative Plastics | ABS | LNP™ THERMOCOMP™ |
| Hostacom EP3307 C12360 | LyondellBasell Industries | PP Copolymer | Hostacom |