PENTAMID AB SK H natur
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTAMID AB |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AI0ykC_PENTAMID-AB-SK-H-natur.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| normal viscosity polyamide 66+6, easy flowing, fast cycle times |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.13 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction | 1.9 | -- | % | ISO 294-4 |
| Flow direction | 1.8 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 8.5 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 3.0 | -- | % | ISO 62 |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 160 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3100 | 1200 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 85.0 | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 5.0 | 20 | % | ISO 527-2 |
| Flexural Modulus | 3100 | -- | MPa | ISO 178 |
| Flexural Stress | 115 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 7.0 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 8.0 | 20 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 90 | -- | kJ/m² | ISO 179/1eU |
| 23°C | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 210 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 70.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 255 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Dielectric Strength (1.00 mm) | 30 | -- | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.20 | -- | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | V-2 | -- | UL 94 | |
| 3.20 mm | V-2 | -- | UL 94 |
| Additional Information |
|---|
| 干燥 ISO Description: PA66+6, MHR, 14-030 NThe value listed as Melting Point, ISO 3146, was tested in accordance with ISO 11357. |
| 调节后的 ISO Description: PA66+6, MHR, 14-030 N |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.14 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 255 - 280 | °C | |
| Middle Temperature | 270 - 285 | °C | |
| Front Temperature | 270 - 280 | °C | |
| Processing (Melt) Temp | 275 | °C | |
| Mold Temperature | 80.0 | °C | |
| Injection Pressure | 50.0 | MPa | |
| Holding Pressure | 30.0 | MPa | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC VNC110E | Vi-Chem Corporation | PVC, Rigid | Vi-Chem PVC |
| 3M™ Dyneon™ PTFE Compound TF 6302 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| LEXAN™ FL930 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| LNP™ THERMOCOMP™ JF006 compound | SABIC Innovative Plastics Europe | PESU | LNP™ THERMOCOMP™ |
| MAJ'ECO EP187L | AD majoris | PP Copolymer | MAJ'ECO |